A) Ferromagnetic domains are perfectly arranged
B) Ferromagnetic domains become random
C) Ferromagnetic domains are not influenced
D) Ferromagnetic material changes into diamagnetic material
Correct Answer: B
Solution :
Beyond curie temperature, ferromagnetic material turns into paramagnetic material, as if ferromagnetic domains become random.You need to login to perform this action.